Polyvinyl alcohol-based photoresist

ABSTRACT

A new photoresist composition suited for fine processing is provided which has practical applications in various dry etching processes. An advantageous pattern formation method using such a photo-resistive composition is also provided. The photoresist composition includes a substance containing a skeleton as at least a part of a main chain. The skeleton is obtained through polymerization of a vinyl alcohol type compound such as a polyvinyl alcohol chain, at least some hydroxyl groups in the skeleton being protected by acid-releasing protective groups. The skeleton preferably contains a group for improving the dry etching resistance. The photoresist composition also includes an optical acid generator. Development with a high polarity solvent, for instance aqueous development, is provided. A positive pattern is obtained by aqueous development, and a negative pattern is obtained by alcohol development.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a photoresistive composition and also to a method of forming a pattern using such a composition. More particularly, the invent ion provides a new photosensitive composition and also a method of forming a pattern using such a photoresistive composition. The photoresistive composition and the pattern formation method according to the invention can be utilized for forming various patterns in the field of fabrication of electronic materials (such as semiconductor devices ).

2. Description of the Related Art

Up to date, there is a trend for finer and denser electronic materials, such as semiconductor devices. For example, the minimum width of semiconductor integrated circuit lines is now going from the order of sub-half micron to the order of quarter micron. To cope with this trend, the lithographic technology, in which the exposure light is short wavelength light of KrF eximer laser (248 nm), ArF eximer laser (193 nm), etc., is attracting attention. Heretofore, various types of photoresists have been proposed for use with such laser beams. For example, chemical amplification type photoresists are attracting attention. A typical chemical amplification photoresist, for instance of positive type, comprises a resin, a dissolution inhibition material and a photo acid generator (i.e., a photo-sensor). In the non-exposed area the dissolution inhibition material is not dissolved in aqueous alkaline solution (i.e., developer) for protecting the resin. But in the exposed area, acid is generated from the photo acid generator, and the dissolution inhibition material is released by this acid to become soluble in the aqueous alkaline solution. The acid acts as a catalyst and hence is not substantially consumed while progressively releasing the dissolution inhibition material. Thus, the photoresist is called chemical amplification type.

At present, however, the various photoresists such as those of the chemical amplification type are actually seldom utilized in various high resolution dry etching processes. (For recent techniques of this kind, see Nozaki et al, 1992 Autumn Proceedings of the Japan Society of Applied Physics, page 504, 17p-ZM-8, and Endo et al "Technical Digest of IEDM", 1992, page 46.)

OBJECTS AND SUMMARY OF THE INVENTION

A first object of the invention is to provide a new photoresist composition, which is suited for fine processes and can be actually utilized for various dry etching processes.

A second object of the invention is to provide an advantageous pattern formation method using such a photoresist composition.

To attain the above objects of the invention, there is provided a photoresist composition, which comprises a substance containing a skeleton as at least a part of a main chain, the skeleton being obtained through polymerization of a vinyl alcohol type compound, at least some hydroxyl groups in the skeleton being protected by acid-releasing protective group, and a photo acid generator. By the term "vinyl alcohol type compound" is meant a compound which gives a polyvinyl alcohol chain (with or without a substitute group).

To attain the objects of the invention, there is also provided a photoresist composition as noted above, in which the substance containing a skeleton as at least a part of a main chain, the skeleton being obtained through polymerization of a vinyl alcohol type compound, at least some hydroxyl groups in the skeleton being protected by acid-releasing protective group, is represented by the following Formula (1) ##STR1## where R is a substitute group, at least some of the substitute groups R being protective groups R⁰ capable of being released by acid.

To attain the objects of the invention, there is further provided a photoresist composition as noted above, in which the substance containing a skeleton as at least a part of a main chain, the skeleton being obtained through polymerization Of a vinyl alcohol type compound, at least some hydroxyl groups in the skeleton being protected by acid-releasing protective groups, is represented by the following Formula (2). ##STR2## where R⁰ is a protective group capable of being released with acid, and R¹ to R⁴ are substitute groups, m:n being 1:9 to 7:3.

To attain the objects of the invention, there is still further provided a photosensitive composition as noted above, in which the substance containing a skeleton as at least a part of a main chain, the skeleton being obtained through polymerization of a vinyl alcohol type compound, at least some hydroxyl groups in the skeleton being protected by acid-releasing protective groups, is represented by the following Formula (3). ##STR3## where R⁰ is a protective group capable of being released by acid, R¹ to R⁴ and R^(1') to R^(4') are substitute groups, m:(n+1) being 1:9 to 7:3.

To attain the objects of the invention, there is yet further provided a method of forming a pattern on an exposure material by using either of the above photosensitive composition, development being done with a high polarity solution. AS the high polarity solution, water or aqueous solution mainly composed of water may be used when obtaining a positive pattern, and various alcohols, typically ethanol, may be used to obtain a negative pattern. It is further possible to obtain a negative pattern with ketones (e.g., acetone). While water or like aqueous solution is used to obtain a positive pattern, it is desirable to make development with hot water at 50° C. or above for realizing satisfactory development.

To attain the objects of the invention, there is further provided a method of forming a pattern as noted above, in which rinsing is done with a low polarity solvent. As the low polarity solvent may be used various organic solvents which do not dissolve the pattern.

Examples of the protective group R⁰ capable of being released by acid as noted above are class 2nd and 3rd alcohol carboxylate represented as ##STR4## substitute groups containing ether bond, such as ethylvinyl ether represented as ##STR5## and tetrahydropyranyl ether represented as ##STR6## and Ac acetate.

According to the invention, the substitute groups R other than R⁰ are suitably those which can enhance the etching resistance. Examples of such group are the adamantyl group represented as ##STR7## norbonyl group as ##STR8## cyclohexyl group as ##STR9## t-butyl group as ##STR10## and cyclopentyl group as ##STR11##

OH (hydroxyl group) and Ac (acetate group) may be present as residue.

Further, R⁰ and other group R may be made integral to provide the following partial acetonide structure. ##STR12##

According to the invention, the skeleton Of the composition may be made more chain-like and less subject to main chain breakage to increase the dry etching resistance. It is thus possible to obtain a photoresist composition, which can find suitable applications as resist materials exclusively used for ArF laser radiation or EB and X-rays.

The main skeleton of the composition according to the invention is obtained through polymerization of a vinyl alcohol type compound such as polyvinyl alcohol and those which are partially esterified (e.g., vinyl acetate). Protective groups for release protection with acid are introduced into a portion of the hydroxyl groups. Further, into a portion of the hydroxyl groups may suitably be introduced adamantyl or like substitute groups which impart with the dry etching resistance as noted above.

The groups that are to be substituted for are as exemplified above. Where the group to be substituted is an ether type protective group, the hydroxyl group is protected by using paratoluene sulfonic acid or like acid catalyst with methylene chloride as the solvent. Where the protective group is a carbonate, the corresponding chloride carbonate is reacted in ether or like solvent by using such basic catalyst as triethylamine, pyridine, etc. Thus, in the above cases the general order of introduction is to introduce first the ether type protective group and then the carbonate.

Where R⁰ and other R are integral and thus providing a partial acetal structure (such as acetonide), reaction with the corresponding acetone and cyclohexane is brought about while azeotropically removing water with benzene or the like by using a Deanstalk type azeotropic apparatus. Further, this type of resin is commercially available as polybutyral resin.

Suitable examples of the protective group R⁰ to be released with acid according to the invention are THP (tetrahydropyranile group), EE (ethylvinyl ether), t-BOC (t-butyl carbonate), etc.

Examples of R¹ to R⁴ and R^(1') to R^(4') are hydrogen, halogen atoms (e.g., Cl), alkyl groups (including substituted alkyl groups, e.g., methyl group, ethyl group, --CH₂ Cl, etc.), allyl group (e.g., phenyl group), --CO.OQ (Q representing methyl group, ethyl group, isopropyl group, butyl group, t-butyl group, cyclohexane group, etc.), --COQ, --OAc, --CN, etc.

The following table shows examples of the combination of R₁ to R₄ to obtain photoresist compositions.

                  TABLE 1                                                          ______________________________________                                         R.sub.1                                                                               R.sub.2                                                                              R.sub.3                                                                               R.sub.4     Material substance                             ______________________________________                                         1    H     H     H    Cl          Vinyl chloride +                                                               vinyl alcohol copo-                                                            lymer (vinyl acetate)                        2    H     H     H    CH.sub.2Cl  Allyl chloride +                                                               vinyl alcohol copo-                                                            lymer (vinyl acetate)                         3    H     H     H                                                                                   ##STR13##   Methyl acrylate + vinyl alcohol copo-                                         lymer (vinyl acetate)                         4    H     H     CH.sub.2                                                                            ##STR14##   Methyl acrylate + vinyl alcohol copo-                                         lymer (vinyl acetate)                        5    H     H     H    COQ         Alkylvinyl ketone +                                                            vinyl alcohol                                                                  copolymer                                    6    H     H     H    Q (Me, Et)  Propylene                                    7    H     H     H    OAc         Partially saponified                                                           vinyl acetate                                 8    H     H     H                                                                                   ##STR15##                                                                                  ##STR16##                                   9    H     H     Cl   Cl          Vinylidene chloride +                                                          alcohol copolymer                                                              vinyl acetate)                               10   H     H     H    Ph          Styrene + vinyl                                                                alcohol copolymer                                                              (vinyl acetate)                              11   H     H     H    H           Ethylene + vinyl                                                               alcohol copolymer                                                              (vinyl acetate)                              ______________________________________                                          Me: methyl group, Et: ethyl group, iPr: isopropyl group, Bu: butyl group,      tBu: tertiary butyl group, Ph: phenyl group, Q: alkyl group              

Further, according to the invention R^(1') to R^(4') can be provided by the above combinations.

Furthermore, according to the invention it is possible to provide photoresistive compositions, which are excellently transparent and suitable as resist materials for KrF or ArF eximer laser. These compositions have high dry etching resistance 3compared to the PMMA type resists.

More specifically, these photoresist compositions are copolymers and are thus very highly heat-resistant, and thus they have high dry etching resistance.

These materials release free hydroxyl groups due to acid generated with light of the acid-releasing protective group, and dissolution of the hydroxyl groups in water gives a pattern.

The weight ratio of the composition can be adjusted by the incorporation ratio or the like. If m is too small, it is undesired because dissolution in water can no longer be obtained.

Copolymerization of the vinyl alcohol units with comonomer mainly permits increase of Tg (glass transition point (softening temperature)) over pure polyvinyl alcohol. Tg tends to be reduced when acid-releasing protective groups are introduced into pure polyvinyl alcohol. Tg can be increased by increasing the molecular weight. With a positive type material, however, it is unsuitable to increase the molecular weight too much.

These materials can be synthesized by introducing protective group through ester exchanges of a vinyl alcohol type compound as the starting material of vinyl alcohol, such as vinyl acetate, and an acetate body, for instance, obtainable through emulsifying copolymerization of the corresponding vinyl compound, with a compound containing corresponding protective group for the portion of hydroxyl group only.

The ester exchange may be made with ##STR17## if the protective group to be introduced is ##STR18##

It may be made with ##STR19## if the protective group is THP.

It may be made with ##STR20## if the protective group is E E (ethyl vinyl ether).

The corresponding acetate body of the material is obtainable by the following method. Vinyl acetate and a vinyl compound are mixed using such an emulsifier as "Noigen YX-500", "Emal-O", etc. The mixture is then polymerized using an aqueous solvent and adding potassium persulfate, ammonium persulfate, etc. and acidic sodium sulfite, sodium sulfonate, sodium phosphate, etc. The polymer is then salted out and then water washed to obtain the acetate body. Such acetate bodies, however, contains alkali metals, and therefore it is preferred to use ammonium bodies.

According to the invention, as the photoacid generator may be used those in Formulas 1 to 13 below. ##STR21##

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a graph showing the relation between normalized thickness and exposure in Embodiment 4 of the invention.

EMBODIMENTS

Embodiments of the invention will be given below without any sense of limiting the invention.

Embodiment 1

Protective groups R⁰ and substitute groups R¹⁰ other than the protective groups as shown in Table 2 below were added in amounts as shown in Table 2 to polyvinyl alcohol resin, and optical acid generators as shown in Table 2 were added in amounts as shown in Table 2. Photoresist compositions were thus obtained, which were photoresist materials capable of development with water.

                                      TABLE 2                                      __________________________________________________________________________     Mole-                                                                          cular         R.sup.0      R.sup.10                                                                           Optical acid                                    weight                                                                               R.sup.0 amount                                                                             R.sup.10 amount                                                                             generator                                       __________________________________________________________________________     A 10000                                                                               ##STR22##                                                                             40%                                                                                 ##STR23##                                                                              40% Tf.sup.⊕ I.sup.⊖ 3%                 B 10000                                                                               ##STR24##                                                                             40%                                                                                 ##STR25##                                                                              40% Tf.sup.⊕ I.sup.⊖ 3%                 C 10000                                                                               ##STR26##                                                                             40%                                                                                 ##STR27##                                                                              40% Tf.sup.⊕ I.sup.⊖ 3%                 D 10000                                                                               ##STR28##                                                                             40%                                                                                 ##STR29##                                                                              40% Tf.sup.⊕ I.sup.⊖ 3%                 E 10000                                                                               ##STR30##                                                                             40%                                                                                 ##STR31##                                                                              40%                                                                                 ##STR32##                                      F 50000                                                                               ##STR33##                                                                             40%                                                                                 ##STR34##                                                                              40% Tf.sup.⊕ I.sup.⊖ 3%                 __________________________________________________________________________      *triphenylsulfonium triflate, shown in Formula 7                         

In this embodiment of the invention, an ArF eximer laser contraction projection exposure apparatus with a contraction factor of 10:1 (manufactured by Raser Ramder Figic) was used, and a 5-inch silicon wafer was used as the pattern formation material.

Each of the resins A to F noted above was dissolved in ethyl cellosolve acetate to produce a coating solution, which was then spin coated on a silicon wafer surface treated with HMDS, followed by baking at 90° C. for 90 seconds to obtain a film with a thickness of 0.7 μm. The film was then exposed using a stepper and by varying the exposure amount and focus using masks with patterns of 0.1 to 0.4μm line-and-space (with a pitch of 0.02). Then, post exposure baking PEB was performed at 110° C. for 90 seconds, then paddle development was done with water: for 60 seconds, and then rinsing was done with xylene.

Etching was done with an Electrochemical reaction (ECR) etcher by using blend gas of Cl₂ and CCl₄. Table 3 below shows the threshold resolution and the etching speed. The etching speed is shown in terms of the speed ratio with the etching speed of m-p cresol novolak with a molecular weight of 5,000 as unity speed.

                  TABLE 3                                                          ______________________________________                                                Threshold resolution                                                                        Etching speed                                              ______________________________________                                         A        0.19 μm line-and-space                                                                     1.2                                                    B        0.21 μm line-and space                                                                     1.6                                                    C        0.20 μm line-and-space                                                                     1.4                                                    D        0.20 μm line-and-space                                                                     1.2                                                    E        0.20 μm line-and-space                                                                     1.2                                                    F        0.25 μm line-and-space                                                                     1.2                                                    ______________________________________                                    

As shown above, in this embodiment it is possible to provide a photoresist composition, which has satisfactory transparency in the ArF eximer laser range, permits satisfactory pattern shape to be obtained and has high dry etching resistance. Besides, development with water is possible, sanitary sewege treatment of organic alkali is unnecessary. It is thus possible to provide a resist material, which is advantageous in view of the environmental safeguarding and can be said to be "kind to the earth".

Embodiment 2

In this embodiment the compositions No. 1 to No. 11 shown in Table 1 noted above were used. The polymerization of the copolymer was set to 1:1. The same exposure material as in Embodiment 1 was used. As the development, paddle development was done with water for 60 seconds. As the baking conditions, pre-baking was done at 100° C. for 100 seconds, PEB was done at 110° C. for 90 seconds, and after-baking was done at 150° C. for 120 seconds. As the solvent, ECA (ethyl cellosolve acetate) was used.

The exposure was done in two ways, when using KrF eximer stepper and when using ArF eximer stepper.

Table 4 below shows the results.

                                      TABLE 4                                      __________________________________________________________________________                                             Protective group:                                                              for t-Bu                                        ##STR35##                                                                                      ##STR36##                                                                                      ##STR37##                                     KrF     ArF     KrF     ArF     KrF     ArF                                        Min.    Min.    Min.    Min.    Min     Min.                               Sensi-                                                                             pattern                                                                            Sensi-                                                                             pattern                                                                            Sensi-                                                                             pattern                                                                            Sensi-                                                                             pattern                                                                            Sensi-                                                                             pattern                                                                            Sensi-                                                                             pattern                    composition No.                                                                        tivity                                                                             (μm)                                                                            tivity                                                                             (μm)                                                                            tivity                                                                             (μm)                                                                            tivity                                                                             (μm)                                                                            tivity                                                                             (μm)                                                                            tivity                                                                             (μm)                    __________________________________________________________________________     1       30  0.30                                                                               40  0.22                                                                               30  0.30                                                                               32  0.25                                                                               70  0.33                                                                               80  0.29                       2       35  0.28                                                                               50  0.20                                                                               25  0.30                                                                               42  0.27                                                                               78  0.32                                                                               88  0.30                       3       20  0.30                                                                               30  0.28                                                                               18  0.32                                                                               32  0.27                                                                               82  0.38                                                                               89  0.36                       4       20  0.30                                                                               32  0.25                                                                               18  0.30                                                                               27  0.28                                                                               80  0.34                                                                               93  0.32                       5       20  0.30                                                                               33  0.25                                                                               18  0.31                                                                               27  0.29                                                                               81  0.34                                                                               74  0.33                       6       40  0.25                                                                               48  0.18                                                                               30  0.28                                                                               36  0.24                                                                               95  0.32                                                                               115 0.28                       7       35  0.27                                                                               40  0.19                                                                               31  0.28                                                                               32  0.23                                                                               92  0.32                                                                               135 0.32                       8       30  0.30                                                                               42  0.20                                                                               21  0.30                                                                               33  0.25                                                                               67  0.35                                                                               170 0.25                       9       30  0.30                                                                               45  0.25                                                                               20  0.30                                                                               37  0.30                                                                               60  0.38                                                                               90  0.30                       10      30  0.40                                                                               70  0.30                                                                               70  0.40                                                                               95  0.40                                                                               135 0.45                                                                               160 0.40                       11      30  0.28                                                                               35  0.22                                                                               25  0.30                                                                               32  0.30                                                                               70  0.30                                                                               100 0.28                       __________________________________________________________________________

As has been shown, in this embodiment it is possible to provide a photoresist capable of development with water, kind to environment, and having excellent dry etching resistance, high Tg, and high permeability to the Ar eximer laser beam (193 nm) and KrF eximer laser beam (248 nm).

Embodiment 3

In this embodiment, butyral resin (1) shown below was used as the substance containing a skeleton as at least a part of a main chain, the skeleton being obtained through polymerization of a vinyl alcohol type compound, at least some hydroxyl groups in the skeleton being protected by acid-releasing protective group. Particularly, the butyral resin used had an acetylation factor of 70 mol % or above. ##STR38##

As the optical acid generator was used the exemplified compound 7 noted above (i.e., triphenylsulfonium triflate).

In this embodiment, 0.18 g of the above optical acid generator is dissolved in ECA (ethyl cellosolve acetate) to obtain 13.08 g of solution. 1.07 g of the above butyral resin (1) was dissolved in this solution, and the resultant solution was passed through a 0.2 μm membrane filter and then spin coated on a Si wafer.

The film thus obtained was pre-heated at 90° C. for 90 seconds. Then, it was exposed to KrF eximer laser beam (or ArF eximer laser beam), and then PEB (post-exposure baking) was done at 80° C. for 90 seconds, followed by development with hot water at 80° C. for several minutes, thus obtaining a satisfactory positive pattern.

The development is done with hot water in order to obtain satisfactory dissolution of the exposed portion if some released groups remained. (see Ichiro Sakurada, Osamu Yoshizaki "Polymer Chemistry" 10,306,310, 1953).

Embodiment 4

The butyral resin (2) used in Embodiment 3 permits a negative pattern to be obtained by development with alcohol.

In this embodiment, the same exemplified compound (triphenylsulfonium triflate) as in Embodiment 3 was used as the optical acid generator. 0.18 g of this optical acid generator was dissolved in ECA (ethyl cellosolve acetate) to obtain 13.08 g of solution. 1.07 g of butyral resin (1) noted above was then dissolved in 1.07 g of the solution, and the resultant solution was passed through a 0.2 μm membrane filter and then spin coated on a Si wafer.

The film thus obtained was pre-baked at 90° C. for 90 seconds. Then, it was exposed as in Embodiment 3, then PEB (post-exposure baking) was done at 110° C. for 90 seconds, followed by development with ethanol for 2 minutes. Thus, satisfactory negative pattern could be obtained. FIG. 1 shows the characteristic (i.e., relation between normalized thickness and exposure). The photoresist composition used in Embodiments 3 and 4 can be said to be suitable for fine processes with KrF or ArF eximer laser beam.

According to the invention, it is possible to provide a new photoresist composition, which is suited for fine processes and can be actually utilized in various dry etching processes. Also, it is possible to provide a method of forming a pattern using such a photoresist composition. 

What is claimed is:
 1. A photoresist composition comprising:(a) a copolymer derived from: ##STR39## alone or in combination with at least one comonomer selected from: ##STR40## wherein R⁰ is selected from ##STR41## groups, R¹⁰ is selected from adamantyl, norbonyl, cyclohexyl, cyclopentyl and t-butyl groups; R¹, R², R³ and R⁴ are selected from hydrogen, halogen, alkyl, chloromethyl, allyl, ##STR42## --COQ, --OAc and --CN groups, wherein Q is alkyl or cycloalkyl, and Ac is acetate; and (b) a photoacid generator, said composition being developable in a polar solution and exhibiting good dry etching resistance.
 2. A composition as defined in claim 1, wherein the mol percent ratio of (i) units to (iv) units present in said copolymer is from about 1:9 to about 7:3, respectively.
 3. A composition as defined in claim 1, wherein said (iv) units are derived from comonomers selected from the group consisting of vinyl chloride vinyl acetate, allyl chloride methyl acrylate, alkylvinyl ketone, ethylene, propylene, acrylonitrile, styrene, vinylidene chloride and partially saponified vinyl acetate. 